Dragon Skin 10 NV

SKU: 800962

Size: Pint Kit
Price:
Sale price$48.95
3

unit(s) in Stock.

5

unit(s) in Stock.

0

unit(s) in Stock.


* Price and availability may vary.
* If unit(s) in stock is 0, item is currently unavailable or special order.

Description

Unit Size Net Weight
Pint Kit 2 lb
Gallon Kit 16 lb
Five Gallon Kit 80 lb

 

 

Dragon Skin 10 NV is a low viscosity, high performance platinum cure silicone rubber that is easy to use and versatile.Mix ratio is 1A:1B by weight or volume, pot life is 15 minutes and cure time is 75 minutes at room temperature. Rubber cures with negligible shrinkage to a Shore 10A. Vacuum degassing is not necessary Color is water white translucent. Dragon Skin 10 NV is suitable for making molds of any configuration for casting plasters, wax, low-melt temperature metal alloys, resins and other platinum silicones (release agent required). Dragon Skin 10 NV is compatible with other Dragon Skin rubbers and is also suitable for special effects applications. Color can be added with Silc Pig or Ignite color pigments. This rubber can be thickened with Thi-Vex thickening agent or softened with SLACKER additive.
Properties
Technical Properties
Mix Ratio by Weight 1A:1B
Mix Ratio by Volume 1A:1B
Pot Life 15 minutes
Cure Time 75 minutes
Color Water White Translucent
Shore Hardness 10A
Mixed Viscosity 6,000 cps
Shrinkage < .001 in./in.
Specific Volume 25.5 cu. in./lb.
Specific Gravity 1.07g/cc
Tensile Strength 400 psi
100% Modulus 27 psi
Elongation @ Break 663%
Die B Tear Strength 90 pli

 

Media

HOW TO MAKE A SEAMLESS RESIN CASTING USING DRAGON SKIN 10 NV
Documentation
Special Order Items
PRODUCT ADVISORY:
The products listed below are currently SPECIAL ORDER items and require pre order.
Lead times may vary - For more information please contact our staff.


800964 - Dragon Skin 10 NV - Five Gallon Kit
Related Products

Payment & Security

Mastercard PayPal Visa

Your payment information is processed securely. We do not store credit card details nor have access to your credit card information.

You may also like