Mold Max 29NV

SKU: 801343

Size: Quart Kit
Price:
Sale price$47.95
13

unit(s) in Stock.

4

unit(s) in Stock.

0

unit(s) in Stock.


*Price and availability may vary.

Description

Unit Size Net Weight
Quart Kit 2.3 lb
Gallon Kit 11.55 lb
Five Gallon Kit 55 lb

 

 

Mold Max 29NV does not require vacuum degassing. Mix ratio is 100A:10B by weight. Working time is 45 minutes and cure time is 6 hours at room temperature. Mold Max 29NV will reproduce the finest detail and is suitable for a variety of industrial and art related applications including making molds for reproducing prototypes, furniture, sculpture and architectural elements. Cure time can be reduced with Accel-T cure accelerator.

Mold Max 29NV can be used to cast a variety of materials including wax, gypsum, low melt alloys/metals and urethane, epoxy or polyester resins.

Important; Do not cast concrete into rubber molds made with this product. Concrete will not cure properly and inhibition will result.

Important; you must weigh Part A & B components using a gram scale to be successful with Mold Max 29NV. Features include: fast cure time 6 hours at room temperature, does not require vacuum degassing, and has a low viscosity for easy mixing and pouring.
Properties
Technical Properties
Mix Ratio by Weight 100A:10B
Mix Ratio by Volume N/A
Pot Life 40 minutes
Cure Time 6 hours
Color Yellow
Shore Hardness 29A
Mixed Viscosity 10,000 cps
Shrinkage 0.002 in./in.
Specific Volume 23.7 cu. in./lb.
Specific Gravity 1.17g/cc
Useful Temperature (max)< 400¼F
Useful Temperature (min)< -65¼F
Tensile Strength 417 psi
100% Modulus 54 psi
Elongation @ Break 361%
Die B Tear Strength 96 pli

 


INSTRUCTIONS

PREPARATION
Safety
Use in a properly ventilated area ("room size" ventilation). Wear safety glasses, long sleeves and rubber gloves to minimize contamination risk. Wear vinyl gloves only. Latex gloves will inhibit the cure of the rubber.

Store and use material at room temperature 73F(23C). Storing material at warmer temperatures will also reduce the usable shelf life of unused material. These products have a limited shelf life and should be used as soon as possible.

Applying a Sealer / Release Agent - Mold Max rubber may be inhibited by sulfur based clays resulting in tackiness at the pattern interface or a total lack of cure throughout the mold. If compatibility between the rubber and the surface is a concern, a small-scale test is recommended. Apply a small amount of rubber onto a non-critical area of the pattern. Inhibition has occurred if the rubber is gummy or uncured after the recommended cure time has passed. To prevent inhibition, a "barrier coat" of clear acrylic lacquer sprayed directly onto the pattern is usually effective. Allow to thoroughly dry.

Although not usually necessary, a release agent will make demolding easier when casting into or over most surfaces. Ease Release 200 is a proven release agent for making molds with silicone rubber and for releasing new silicone from cured silicone.

Because no two applications are quite the same, a small test application to determine suitability for your project is recommended if performance of this material is in question.

MEASURING & MIXINGMaterials should be stored at about 73F(23C). These products have a limited shelf life and should be used as soon as possible. Wear safety glasses, long sleeves and rubber gloves to minimize contamination risk. Before you begin, pre-mix Part A (base) thoroughly to re-disperse fillers that may have settled. Using a gram scale, dispense required amounts of parts A and B into a mixing container and mix for 3 minutes. Scrape the sides and bottom of the container several times.

POURINGFor best results, pour your mixture in a single spot at the lowest point of the containment field. Let the rubber seek its level up and over the model. A uniform flow will help minimize entrapped air. The liquid rubber should level off at least .5" (1.3 cm) over the highest point of the model surface.

CURING & PERFORMANCECuring / Post Curing - Allow the mold to cure fully (at least 6 hours) at room temperature 73F(23C) before demolding. Post curing the mold an additional 4 hours at 150F(65C) will eliminate any residual moisture and alcohol that is a by-product of the condensation reaction that can inhibit the cure of some resins and rubbers. Allow mold to cool to room temperature before using. Do not cure rubber where temperature is less than 65F(18C).

Accelerating Mold Max 29NV - Accel-T tin cure silicone rubber accelerator will accelerate the cure time of Mold Max 29NV. Note: working time is reduced in proportion to the amount of Accel-T added. Thinning Mold Max 29NV - Silicone Thinner is a non-reactive silicone fluid that will lower the mixed viscosity of tin cure (condensation) or platinum cure (addition) silicone rubber products. Silicone Thinner offers the following advantages: [1] A lower mixed viscosity (A+B) means that the rubber will de-air faster when vacuuming; [2] Mixed rubber (A+B) will flow better over intricate model detail; [3] Silicone Thinner will lower the ultimate shore hardness (durometer) of cured silicone rubber; [4] Pot life (working time) is increased in proportion to the amount of Silicone Thinner used.A disadvantage is that ultimate tear and tensile are reduced in proportion to the amount of Silicone Thinner added, however knotty tear properties of the Mold Max Series rubbers are unaffected. It is not recommended to exceed 10% by weight of total system (A+B). See the Silicone Thinner technical bulletin for full details.

Making Brush-On Rubber Molds - Due to low viscosity, Mold Max 29NV is not recommended for making brush-on rubber molds. If you want to make a brush-on rubber mold, Mold Max Stroke was developed especially for this purpose.

Mold Performance & Storage - The physical life of the mold depends on how you use it (materials cast, frequency, etc.). Casting abrasive materials such as concrete can quickly erode mold detail, while casting non-abrasive materials (wax) will not affect mold detail. Before storing, the mold should be cleaned with a soap solution and wiped fully dry. Two part (or more) molds should be assembled. Molds should be stored on a level surface in a cool, dry environment.
Media

Recreating an Antique Frame Using Mold Max 29NV No Vacuum Required Silicone Rubber
Documentation
Special Order Items
PRODUCT ADVISORY:
The products listed below are currently SPECIAL ORDER items and require pre order.
Lead times may vary - For more information please contact our staff.


801345 - Mold Max 29NV - Five Gallon Kit
Related Products

Payment & Security

Mastercard PayPal Visa

Your payment information is processed securely. We do not store credit card details nor have access to your credit card information.

You may also like