Flex Foam-iT 14 Lb

SKU: 799904

Size: Pint Kit
Sale price$50.99


Unit Size Net Weight
Pint Kit 2.9 lb
Gallon Kit 23.2 lb
Five Gallon Kit 116 lb



FlexFoam-iT 14 is a premium quality water blown flexible foam that can be used for a variety of industrial, special FX, arts and crafts projects. Applications include making of theatrical props (swords, knives, hammers, etc.), industrial gaskets, custom padding and cushioning and more. SO-Strong colorants may be added for coloring effects. Part A & B liquids are combined, mixed, and poured into a mold or other form (apply release agent if necessary). Mixture will rise and cure quickly to a solid, flexible foam.
Technical Properties
Mix Ratio by Weight 100A:190B
Mix Ratio by Volume 1A:2B
Pot Life 60 seconds
Tack Free Time 45 minutes
Cure Time 2 hours
Color White
Mixed Viscosity 1,000 cps
Specific Volume 114 cu. in./lb.
Specific Gravity 0.22g/cc
Expansion (Approx.) 4 times
Foam Density 14 lb./cu. ft.



Thorough pre-mixing of both Part"A" and Part"B" in their original containers prior to measuring out. Specifically, failure to pre-mix Part"B" prior to dispensing will cause the ingredients in the system to remain unbalanced. Storing and working with materials in cold environments will cause the components of Parts "A" and "B" to separate (i.e. vinegar and oil). If these components are not brought back to proper room temperature and reconstituted this will cause failure in their cross-linking when mixed together.
Thorough mixing of Part"A" and Part"B" combined.Once combined together, Part"A" and Part"B" must be evenly and thoroughly blended scraping both sides and bottom of the mixing container. A double-mix pour technique, time allowing depending on product blended pot-life, will assist in the most successful mixing technique. Often with the foams, users will work quickly as materials generally have a short pot-life before expansion occurs and neglect a thorough mixing procedure.
Use of silicone-based release agents in molds where foams are cast, will cause collapse of the foam cell structure.
Mold configuration; if the mold is 'closed' and not capable of allowing gas to escape during the expansion & cure process of the foam, the de-molding procedure will result in the gases escaping from the cured foam causing collapse of the casting. Using a mold where the gases are allowed to escape during cure is important.
If the casting comes out of the mold collapsed; often it can be compressed which will cause it to re-inflate.
Cold molds can also contribute to foam collapse; sometimes materials will be kept at proper temperature, however, if the material is poured into a cold mold, that may cause cure-issues and collapse of the foam casting.
How To Improve The Surface Finish Of Foam Castings Using Back Pressure

Special Order Items
The products listed below are currently SPECIAL ORDER items and require pre order.
Lead times may vary - For more information please contact our staff.

799906 - Flex Foam-iT 14 Lb - Five Gallon Kit
Related Products

Payment & Security

Mastercard PayPal Shop Pay Visa

Your payment information is processed securely. We do not store credit card details nor have access to your credit card information.

You may also like